タイトル: Mechanism of corrosion resistance degradation of Cr-plated parts due to heat treatment and its prevention
著者: Kobayashi, Yuichi
Nagasawa, Junichi
Sasaki, Toshihiko link image link image
Hirose, Yukio link image
佐々木, 敏彦
広瀬, 幸雄
発行日: 2003年 3月15日
出版社(者): 日本材料学会
雑誌名: Materials Science Research International
ISSN: 1341-1683
巻: 9
号: 1
開始ページ: 94
終了ページ: 101
キーワード: Corrosion resistance
Cr-Plating layer
Heat treatment
Postfinishing
Residual stress
X-ray stress measurement
抄録: The mechanism of decrease in the corrosion resistance of Cr-plated parts when they are subjected to a heating process and measures for preventing the degradation are studied. When postfinishing is performed after the Cr-plating process, cracks in the Cr layer are closed as a result of plastic flow on the topmost surface layer. When the residual stress in the Cr layer becomes compressive due to the postfinishing, the cracks are completely closed, resulting in a high corrosion resistance. The residual stress in the Cr layer changes from compressive to tensile following heat treatment. When the residual stress becomes tensile, the cracks in the Cr layer which were closed during postfinishing open once again, resulting in a decrease in the corrosion resistance. We speculated that the change of residual stress from compressive to tensile is caused by the shrinkage of the Cr layer due to heat treatment and the difference in the coefficients of thermal expansion between the substrate (steel) and Cr layer, as well as the release of residual stress generated during processing. In order to prevent the decrease of corrosion resistance under heat treatment, it is effective to apply compressive stress which exceeds the level of change in residual stress due to heat treatment to the Cr layer during postfinishing, after the Cr plating process.
URI: http://hdl.handle.net/2297/12312
関連URI: http://ci.nii.ac.jp/naid/110002284026/
資料種別: Journal Article
権利関係: 日本材料学会;本文データは日本材料学会の許諾に基づきCiNiiから複製したものである
版表示: publisher
出現コレクション:1.査読済論文(工)

このアイテムを引用あるいはリンクする場合は次の識別子を使用してください。 http://hdl.handle.net/2297/12312

本リポジトリに保管されているアイテムはすべて著作権により保護されています。

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - ご意見をお寄せください